NM360 wear-resistant steel is widely used in mining machinery, mining machinery, environmental protection machinery, engineering machinery, also used as the yield strength ≥700MPa high-strength structural steel. Range: belongs wear plate (wear plate) series. Name: N resistant (nai) M is the mill (mo) of two first phonetic alphabet Chinese characters, 360 represents the average Brinell hardness of this steel heat treatment: tempering, quenching and tempering (quenching) Role: The main is to provide the occasion or location need to wear protection equipment, longer life, reduced maintenance downtime caused by maintenance, and the corresponding reduction in capital investment. Performance: yield in more than 800, the tensile strength in 1000. Wear plates purposes: 1) thermal power plant: pulverizers cylinder liner, fan impeller nest shell, ESP inlet flue ash catheter, turbine bucket liner, separator connection pipe, coal crusher liner , coal hopper and crusher liner, burner tip, off the coal bucket and funnel liner, air pre-heater powered support tile, guide vane separator. It said parts of the hardness and abrasion resistance of wear-resistant steel not too high demands, you can use the material for the wear-resistant steel plate NM360 / 400 6-10mm in thickness. 2) coal field: chute and funnel lining, hopper bush, fan blades, pusher plate, cyclone dust collector, coke guide liner, ball mill liners, drill stabilizer, screw feeder bell and base seat, kneading machine bucket liners, ring feeders, dumpers floor. Poor coal field operating environment, corrosion resistance and abrasion resistance of wear-resistant steel have certain requirements, recommended material for NM400 / 450 HARDOX400 8-26mm thickness of wear-resistant steel. 3) cement plant: chute liners, the end of the bush, cyclone dust collector, separator blades and vanes, fan blades and liners, recycling bucket liners, floor screw conveyor, pipeline components, frit cooling pan lining, trough liner. These components are also required wear resistance, corrosion wear-resistant steel plate a little better, you can use the material as NM360 / 400 HARDOX400 8-30mmd thickness of wear-resistant steel. 4) loading machine: unloading mill chain plate, hopper linings, grab edge board, automatic dump truck dump plate, dump truck bodies. This requires a very high abrasion resistance and hardness of wear-resistant steel, it is recommended to use the material as NM500 HARDOX450 / 500 25-45MM thickness of wear-resistant steel. 5) Mining Machinery: mineral aggregate, stone crusher liner, blade, conveyor liner, the baffle. Such components need high wear resistance, it can be made of NM450 / 500 HARDOX450 / 500 10-30mm thickness of wear-resistant steel. Chemical composition: This is Wugang enterprise standards: WYJ112-2008 chemical composition component manufacturers C Si Mn PS Cr Mo Ni B grades WNM360 Wugang ≤0.25 ≤0.70 ≤1.30 ≤0.025 ≤0.010 ≤1.4 ≤0.50 ≤1.00 ≤0.004 mechanical properties: This is Wugang enterprise standards: WYJ112-2008 manufacturers hardness grades and mechanical properties of tensile properties 20 ℃ AKV lateral J RP0.2 Rm A50% MPa MPa WNM360 Wugang 320 ~ 400 ≥800 ≥1000 ≥10 provide physical performance yield strength steel plate about In 1000MPa, tensile strength of about 1100MPa. abrasion resistant steel Wugang NM360 16 2200 10000 2.763 quenched wear resistant steel plate NM360 16 2200 10000 2.763 Wugang quenched and tempered abrasion resistant steel plate NM360 16 2200 10000 2.763 Wugang quenched and tempered abrasion resistant steel plate NM360 16,220,010,000 2.763 quenched abrasion resistant steel Wugang NM360 16 2200 10000 2.763 quenched abrasion resistant steel Wugang NM360 16 2200 10000 2.763 quenched abrasion resistant steel Wugang NM360 16 2200 10000 2.763 quenched abrasion resistant steel Wugang NM360 16 2200 10,000 2.763 quenched abrasion resistant steel Wugang NM360 20 2200 10000 3.454 quenched abrasion resistant steel Wugang NM360 20 2200 10000 3.454 quenched abrasion resistant steel Wugang NM360 20 2200 10000 3.454 quenched abrasion resistant steel Wugang NM360 20 2200 10000 3.454 Wugang quenched and tempered abrasion resistant steel plate NM360 20 2200 10000 3.454 Wugang quenched and tempered abrasion resistant steel plate NM360 20 2200 10000 3.454 Wugang quenched